Application of ER316, ER316L, ER316Lsi, H0Cr19Ni12Mo2, H0Cr19Ni12Mo2, Y316Lsi, Y316, Y316L Stainless Steel Welding Wire:
ER316/ER316L:
Used for welding 10Cr-12Ni-2.5Mo (SUS316) steel;
For welding heat exchanger tubes and furnace tubes with the working temperature of 600~750 ℃ in chemical oil refining fields;
Stable welding arc and beautiful weld pass appearance;
Its oxidation resistance temperature is not less than 870 ℃.
ER316LSi: Primarily used for welding of high silicon, low carbon, 18Cr - 12Ni - 2.5Mo steels.
Standard-compliant:
| AWS:ER316 | YB/T:H0Cr19Ni12Mo2 | JIS:Y316 |
| AWS:ER316L | YB/T:H0Cr19Ni12Mo2 | JIS:Y316L |
| AWS:ER316LSi | JIS:Y316LSi |
Technical Parameters of ER316, ER316L, ER316Lsi, H0Cr19Ni12Mo2, H0Cr19Ni12Mo2, Y316Lsi, Y316, Y316L Stainless Steel Welding Wire:
| Wire Type | Wire Size | Spool Size | Net Weight | ||||||
| MIG Wire | φ0.8~1.6(mm) | D100mm D200mm D300mm D270mm | 1kg 5kg 15kg 20kg | ||||||
| TIG Wire | φ1.6~5.0(mm) | Straight wire length: 1 meter | 5kg 10kg | ||||||
| Chemical Composition of Welding Wire (%) | |||||||||
| Type | Mechanical Properties or Deposited Metal | C | Si | Mn | Cr | Ni | Mo | Other | |
| Tensile Strength σb(Mpa) | Elongation δ5 (%) | ||||||||
| ER316 | 578 | 38 | 0.050 | 0.60 | 1.78 | 19.61 | 12.50 | 2.20 | - |
| ER316L | 590 | 40 | 0.025 | 0.42 | 1.91 | 19.10 | 12.58 | 2.57 | - |
| ER316LSi | 562 | 31 | 0.021 | 0.77 | 1.95 | 19.20 | 13.45 | 2.58 | - |
| Note | Welding Position | ||||||||
| Welding wire should be stocked in dry environment. Open the packs just when welding to avoid the wire rust. | |
||||||||
| Before welding, please clean out the oil, rust, water etc from the welding surface. | |||||||||