ER49-1, H08Mn2SiA Mild Steel Welding Wire

Description of ER49-1 Mild Steel Welding Wire:
Under the protection of the copper layer, this ER49-1Mild Steel Welding Wire is with high anti-corrosion ability and excellent welding properties. Based on the combined deoxidation of Mn\Si, the welding seams have excellent mechanical properties without weld porosity and slag appearance.

Application of ER49-1, H08Mn2SiA Mild Steel Welding Wire:
Being an important welding supplies for welding process, it is widely used for CO2 gas shielded semi-automatic and automatic welding to produce marine boilers, marine pipelines, marine cargo, deck and container, which are made of ship building steel (A32, E32, D32, A36, E36, D36) and plain low carbon steel with strength at 490N/mm2 degree, as well as mild alloy steel 16Mn, 15Mn etc.

Standard-compliant:
GB/T: ER49-1　H08Mn2SiA

Technical Parameters of ER49-1, H08Mn2SiA Mild Steel Welding Wire:

Packaging		Wire Size		Spool Size				Net Weight
		φ0.8~1.6(mm)		D100mm D200mm D270mm D300mm K300mm				1kg, 5kg, 15kg, 18kg, 20kg
Chemical Composition of Welding Wire (%)		C	Mn	Si	P	S	Cr	Ni	Cu
		≤0.11	1.80~2.10	0.65~0.95	≤0.030	≤0.030	≤0.20	≤0.30	≤0.50
Mechanical Properties or Deposited Metal		Yield Strength σ0.2(Mpa)		Tensile Strength σb(Mpa)		Elongtationδ5 (%)		AKV Impact (J)
		≥372		≥490		≥20		≥47(Room temperature)
Welding Wire Diameter (mm)		φ0.8	φ1.0	φ1.2	φ1.6	Welding Position
Welding Current (AMP.)		40~140	50~220	80~350	120~450
Note		Welding wire should be stocked in dry environment. Open the packs just when welding, so as to avoid the wire rust.
		Before welding, please clean out the oil, rust, water etc from the welding surface.